Shijiazhuang Shuanglu Machinery Co., Ltd.("Shuanglu" and "SUNLU" for short), as a member of China Welding Association (CWA) and one of the appointed manufacturers of China National Electric Equipment Corporation (CNEEC), manufactures complete welding electrode product.
Packaging & Shipping
2.5mm:2.5kg/box, 20kg/box, 2tons/pallet.
3.2mm:5kg/box, 20kg/box, 2 tons/pallet.
4.0mm:5kg/box, 20kg/box, 2 tons/pallet.
5.0mm:5kg/box, 20kg/box, 2 tons/pallet.
Or Customize!
Product Description
Introduction:
E308L-16 is a kind of ultra-low-carbon Cr18Ni12Mo2 stainless steel electrode with lime-titania type coating. The carbon content of the deposited metal is lower than or equal to 0.04%. It has excellent heat-resistance, corrosion-resistance, crack-resistance, blowhole-resistance and welding performance. The coating has red-resistance and high strength. AC/DC.
Uses:
Used for welding equipment of urea, synthetic fiber, etc. and stainless steel structures of the same types, and also used for Cr stainless steel which does not need heat treatment after welding, composite steel, dissimilar steel, etc.
Chemical Composition of Deposited Metal (%)
Chemical Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Guarantee Value
≤0.04
0.5~2.5
≤0.90
≤0.020
≤0.030
11.0~14.0
≤0.75
17.0~20.0
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
A(%)
-196℃ KV2(J)
Guarantee Value
≥490
≥30
≥32
Reference Current (AC, DC+)
Electrode Diameter(mm)
φ2.0
φ2.5
φ3.2
φ4.0
φ5.0
Welding Current (A)
25~50
50~80
80~110
130~160
160~200
Instructions: 1.The electrodes should be baked under 250-300℃ for an hour before welding. 2.Direct current had better be used and the current should not be too strong.
More detailed and photos, please check our website: